Nickel 200/201 Sheets & Plates
- Home
- :
- Grades
- :
- Nickel Alloys
- :
- Nickel 200/201 Sheets & Plates
Grades
Nickel 200/201 Sheets & Plates
Nickel 200 and Nickel 201 plates and sheets are high-purity, solid-solution nickel alloys known for their exceptional corrosion resistance, particularly in reducing environments. They offer excellent resistance to various corrosive substances, including acids and alkalis. These materials are often used in industries such as chemical processing, electronics, and aerospace, where their high thermal and electrical conductivity, along with their low electrical resistivity, make them valuable. Nickel 200 and Nickel 201 sheets and plates come in various sizes and thicknesses, suitable for a wide range of applications, from fabricating equipment components to lining tanks and vessels in corrosive environments.
Nickel 200 Sheets offer high corrosion resistance, much better than alloy, because to the presence of columbium. Because the required standard will be fully met as specified on the order, the chemical composition of Nickel 200 Plates may vary somewhat between different product standards. We are the leading manufacturers of Nickel 200 Coils, which come in a variety of diameters and lengths to meet your needs. Nickel 201 Sheets are commonly used for parts that are intermittently heated up to 1500 degrees Fahrenheit, with a maximum temperature of 1650 degrees Fahrenheit for continuous service. Only cold reduction in Nickel 201 Plates can take advantage of the alloy’s superior qualities. Nickel 201 Coils offer similar resistance to general, overall corrosion as the unsterilized chromium nickel Alloy.
Alloy 200 Sheets contain columbium and tantalum, which provide some desirable properties. Alloy 200 Plates are primarily employed in applications where corrosion resistance and long-term operation at temperatures ranging from 800 to 1600 degrees Fahrenheit are critical. In a petrochemical plant, Alloy 200 Coils must have appropriate creep resistance, hot corrosion resistance, and fatigue resistance.
Specifications
Material Grade: Nickel 200 or Nickel 201
Standard Dimensions: Various sizes and thicknesses are available, depending on the specific application requirements.
Purity: These alloys have high levels of purity, with Nickel 200 having a minimum of 99.0% nickel and Nickel 201 having a minimum of 99.6% nickel.
Corrosion Resistance: Excellent resistance to various corrosive environments, including acids and alkalis.
Mechanical Properties: Specifications for tensile strength, yield strength, and elongation may vary based on the manufacturer’s standards.
Temperature Range: These alloys maintain their properties at elevated temperatures and are suitable for high-temperature applications.
Standards: Nickel 200 and Nickel 201 plates and sheets may adhere to industry standards like ASTM B162 for plates and ASTM B162 for sheets.
size range
Thickness – 1mm to 25mm
Width – standard – 1219mm, 1250mm, 1500mm, 2000mm wide
Length – 2500, 3000, 6000mm long
Material Certification and Traceability
At Satyam Overseas, we prioritize Material Certification and Traceability. Our materials, meeting ASTM and ASME standards, come with 3.1 Mill Test Certificates as a guarantee of compliance. Additionally, upon request, we provide 3.2 Mill Test Certificates for added assurance. Every material is clearly marked and accompanied by a corresponding certificate, meticulously linking markings to certification. This meticulous approach ensures complete accountability and unwavering reliability throughout our supply chain.
Chemical Composition
Nickel 200
| Nickel | Copper | Iron | Manganese | Carbon | Silicon | Sulfur | |
|---|---|---|---|---|---|---|---|
|
Min |
99.0 |
– |
– |
– |
– |
– |
– |
|
Max |
– |
0.25 |
0.40 |
0.35 |
0.15 |
0.35 |
0.01 |
Nickel 201
| Nickel | Copper | Iron | Manganese | Carbon | Silicon | Sulfur | |
|---|---|---|---|---|---|---|---|
|
Min |
99.0 |
– |
– |
– |
– |
– |
– |
|
Max |
– |
0.25 |
0.40 |
0.35 |
0.02 |
0.35 |
0.01 |
Physical Composition
Nickel 200
| Density, lb/in 3 | Density, g/cm 3 | Melting Range, °F | Melting Range, °C | Specific Heat, Btu/lb•°F | Specific Heat, J/kg•°C | Curie Temperature, °F | Curie Temperature, °C |
|---|---|---|---|---|---|---|---|
|
0.321 |
8.89 |
2615-2635 |
1435-1446 |
0.109 |
456 |
680 |
360 |
Nickel 201
| Density, lb/in 3 | Density, g/cm 3 | Specific Heat, Btu/lb•°F | Specific Heat,J/kg•°C | Curie Temperature, °F | Curie Temperature, °C | Modulus of Elasticity (Tension), 103 ksi | Modulus of Elasticity (Tension), GPa |
|---|---|---|---|---|---|---|---|
|
0.321 |
8.89 |
0.109 |
456 |
680 |
360 |
60 |
207 |
Designations & Standards
| Forms | ASTM | ASME | DIN |
|---|---|---|---|
|
Plate, Sheet & Strip |
B 162 |
SB 162 |
17750 |